APPLIED STUDIES ON MATERIAL OF BIOCOMPOSITE BIOLOGICAL ORIGIN PREPARED FROM OXIDE NANO AND BIOGUM (EXTRACTED FROM OSAKA SEEDS) FOR THE TREATMENT OF METHYLENE BLUE/ NGUYEN TRA PHUONG NHUNG...[VÀ NHỮNG NGƯỜI KHÁC], TẠP CHÍ ĐẠI HỌC THỦ DẦU MỘT, SỐ 1(40),2019,TR.3-10
Researching on Methyllen Blue dye treatment ability with Nano material (CoFe2O4 synthesized by co-precipitation method) combined with Biogum (extracted from Osaka Seeds (Cassia Fistula Linn). Research results show that with Biogum base material fully covered by magnetic nanoparticles of size 70-95 nm (SEM) and the presence of several specific functional groups for biogum and ferromagnetic oxide nano (FT-IR). When adding OH group to nano material, the adhestive ability to biogum and the size of the particle does not change. Results of comparative studies on the application of Nano-Biogum and Nano-OH-Biogum materials showed that when studying the dyeing color of Methylene blue, the treatment efficiency is from 62.43 to 78.72%, decreasing from 349.67 Pt-Co. 74.41 Pt-Co at pH 6-7 and dosage at 1.5 g/l. Based on the above results, Nano -Biogum is able to treat dyeing color better than Nano OH -Biogum. Therefore, Nano -Biogum can become suitable material for the application of color treatment in practice.
Xin lỗi bạn không thể down load tài liệu này. Bạn có thể xem tài liệu trực tuyến trên website hoặc liên hệ thư viện trường để được hướng dẫn. Cảm ơn bạn đã sử dụng dịch vụ của chúng tôi.
Bạn vui lòng tham khảo thỏa thuận sử dụng của thư viện số.